Preheated acid associated with silane and electric current in the adhesion of the resin cement to ceramic

Abstract This study verified the effect of the combination of preheated hydrofluoric acid/silane/electric current in the adhesion of the resin cement to ceramic. IPS E.max Press ceramic discs embedded in PVC rigid tubes were divided into four groups associating preheated hydrofluoric acid and silane applied with electrical current (n=10): Ha+S (Heated acid + silane); Ha+S+Ec (Heated acid + silane + electrical current); A+S (Acid + silane) and A+S+Ec (Acid + silano + electrical current). Resin cement/ceramic samples were stored in water at 37°C for 24h. After storage, they were submitted to the microshear test, fracture analysis, and contact angle at 24h or after thermocycling (10,000 cycles/5-55ºC). Bond strength data were evaluated by two-way ANOVA. For comparison between evaluation times (24h or thermocycling) was applied unpaired t-test. A significance post-hoc test of p=0.05 was assumed for analyses and graphs (GraphPad Prism 9.0 software). At 24h, the microshear strength showed similar values between Ha+S, Ha+S+Ec, and A+S+Ec groups, while A+S showed the lowest value with a statistical difference. After thermocycling, Ha+S and Ha+S+Ec were similar, as well as A+S and A+S+Ec. There was a significant difference in all groups comparing 24h (highest value) with after thermocycling (lowest value). Adhesive fracture was predominant in all groups and evaluation times. Ha+S and A+S groups showed higher contact angle values compared to the Ha+S+Ec and A+S+Ec with lower values. In conclusion, the association of preheated hydrofluoric acid/silane applied or not with electric current promoted different microshear strength values, fracture types, and contact angles in the resin cement/ceramic bond.

Resumo Este estudo verificou o efeito da combinação ácido fluorídrico pré-aquecido/silano/corrente elétrica na adesão do cimento resinoso à cerâmica. Os discos cerâmicos IPS E.max Press embutidos em tubos rígidos de PVC foram separados em quatro grupos associando ácido fluorídrico pré-aquecido e silano aplicado com corrente elétrica (n=10): Ha+S (ácido aquecido + silano); Ha+S+Ec (Ácido aquecido + silano + corrente elétrica); A+S (Ácido + silano) e A+S+EC (Ácido + silano + corrente elétrica). Amostras de cimento resinoso/cerâmica foram armazenadas em água a 37°C por 24 horas. Após o armazenamento foram submetidas ao ensaio de micro cisalhamento, análise de fratura e ângulo de contato no período de 24 horas ou após termociclagem (10.000 ciclos/5-55ºC). Os dados de resistência de união foram avaliados por ANOVA dois fatores. Para comparação entre os tempos de avaliação (24 horas ou termociclagem) foi aplicado o teste t não pareado. Foi assumida significância de 5% para análises e gráficos (software GraphPad Prism 9.0). Em 24 horas, a resistência ao micro cisalhamento apresentou valores similares entre os grupos Ha+S, Ha+S+Ec e A+S+Ec, enquanto A+S apresentou menor valor com diferença estatística. Após a termociclagem, Ha+S e Ha+S+Ec foram similares, assim como A+S e A+S+Ec. Houve diferença significativa em todos os grupos comparando 24 horas (maior valor) com após termociclagem (menor valor). A fratura adesiva foi predominante em todos os grupos e tempos de avaliação. Os grupos Ha+S e A+S apresentaram maiores valores de ângulos de contato comparados aos grupos Ha+S+Ec e A+S+Ec com valores menores. Em conclusão, a associação ácido fluorídrico pré-aquecido/silano aplicado com corrente elétrica promoveu diferentes valores de resistência ao micro cisalhamento, tipos de fratura e ângulos de contato na adesão do cimento resinoso à cerâmica.

Effect of Ceramic Thickness on the Bond Strength to Resin-Luting Agents before and after Thermal Cycling

Abstract This study investigated microshear bond strength (µSBS) of two (2) dual-cured resin-luting agents (RelyX™ Ultimate and RelyX™ U200) when photoactivated through varying thicknesses of lithium disilicate, with or without thermal cycling. Discs of IPS e.max Press of 0.5, 1.5, and 2 mm in thickness were obtained. Elastomer molds (3.0 mm in thickness) with four cylinder-shaped orifices 1.0 mm in diameter, were placed onto the ceramic surfaces and filled with resin-luting agents. A Mylar strip, glass plate, and load of 250 grams were placed over the filled mold. The load was removed and the resin-luting agents were photoactivated through the ceramics using a single-peak LED (Radii Plus.) All samples were stored in distilled water at 37oC for 24 h. Half of the samples were subjected to thermal cycling (3,000 cycles; 5ºC and 55ºC). All samples were then submitted to µSBS test using a universal testing machine (Instron 4411) at a crosshead speed of 0.5 mm/min. Data were submitted to three-way ANOVA and Tukey post-hoc test (α=0.05). The mean µSBS at 24 h was significantly higher than after thermal cycling (p<0.05). No statistical difference was found between resin-luting agents (p > 0.05). The mean µSBS for groups photoactivated through 0.5 mm ceramic were significantly higher than 1.5 mm and 2.0 mm (p < 0.05). In conclusion, increased ceramic thicknesses reduced the bond strength of tested resin-luting agents to lithium disilicate. No differences were found between resin-luting agents. Thermal cycling reduced the bond strength of both resin-luting agents.

Resumo: Este estudo investigou a resistência de união ao microcisalhamento (RUµC) de dois (2) agentes de cimentação de resina dual (RelyX™ Ultimate e RelyX™ U200) quando fotoativados através de diferentes espessuras de dissilicato de lítio, com ou sem ciclagem térmica. Discos do IPS e.max Press de 0,5, 1,5 e 2 mm de espessura foram obtidos. Moldes de elastômero (3,0 mm de espessura) com quatro orifícios cilíndricos de 1,0 mm de diâmetro foram colocados sobre as superfícies cerâmicas e preenchidos com agentes de cimentação de resina. Uma tira Mylar, placa de vidro e carga de 250 gramas foram colocadas sobre o molde preenchido. A carga foi removida e os agentes de cimentação resinosos foram fotoativados através da cerâmica usando um LED de pico-único (Radii Plus). Todas as amostras foram armazenadas em água deionizada a 37oC por 24 h. Metade das amostras foi submetida a ciclagem térmica (3.000 ciclos; 5ºC e 55ºC). Todas as amostras foram então submetidas ao teste de RUµC usando uma máquina de teste universal (Instron 4411) com velocidade de 0,5 mm/min. Os dados foram submetidos à Análise de Variância três fatores e ao teste post-hoc de Tukey (α = 0,05). A média de RUµC em 24 h foi significativamente maior do que após a ciclagem térmica (p < 0,05). Não houve diferença estatística entre os cimentos resinosos (p > 0,05). As médias de RUµC para grupos fotoativados através de cerâmica de 0,5 mm foram significativamente maiores do que 1,5 mm e 2,0 mm (p < 0,05). Em conclusão, o aumento da espessura da cerâmica reduziu a resistência de união dos agentes de cimentação resinosos ao dissilicato de lítio. Não foram encontradas diferenças entre os agentes de cimentação resinosos. A ciclagem térmica reduziu a resistência de união de ambos os agentes de cimentação resinosos.

Dental displacement in complete dentures influenced by different flask types and polymerization cycles

Abstract This study evaluated the dental displacement in dentures included in different flasks and processed by the Australian cycle modified or by microwave. Metal pins were placed on the teeth as reference for measurements: a) Incisal edge of maxillary and mandibular central incisors, buccal cusp of maxillary and mandibular vestibular first premolars, and mesiobuccal maxillary and mandibular cusps of second molars; b) Incisor to incisor, premolar to premolar and molar to molar; c) Left incisor to left molar and right incisor to right molar, and d) Vertical. Dentures were divided according to flasks (n=10): G1- Metal; G2- HH bimaxillary metal; G3-Microwaves; G4- HH bimaxillary microwaves. For G1 and G2, polymerization at 65ºC/30 min, flame quenched for 30 min, heating at 65ºC/30 min, boiling water for 1 h. For G3 and G4, microwave (20 min/140 W and 5 min/560 W). Comparator microscope with digital camera and analytical unit assessed the measurements before and after denture polymerization. The final distance was made subtracting the distance before the denture processing from the distance of the dental displacement after processing. The value of the difference was submitted to 2-way ANOVA, considering the flask type and denture type. Maxillary denture showed greater displacement when compared to mandibular denture. Flask types and interaction with denture types showed similar difference between before and after polymerization. In conclusion, displacement promoted by flask types in dentures cured by polymerization cycles promoted similar effect on the distance between teeth. Greater value for distance between teeth occurred for maxillary denture.

Resumo O objetivo neste estudo foi avaliar o deslocamento dental em próteses totais incluídas em diferentes tipos de muflas e polimerizadas pelo ciclo australiano ou por micro ondas. Pinos metálicos foram colocados nos dentes como pontos de referência para as medidas: a) Borda incisal dos incisivos centrais maxilares e mandibulares, cúspide vestibular dos primeiros pré molares maxilares e mandibulares e cúspides mésiovestibulares dos segundos molares maxilares e mandibulares; b) Distâncias látero-laterais incisivo a incisivo, pré-molar a pré-molar e molar a molar; c) Distâncias horizontais anteroposterior incisivo esquerdo a molar esquerdo e incisivo direito a molar direito, e d) Vertical. As próteses foram separadas de acordo com o tipo de mufla (n=20): G1- Metálica; G2-HH bi-maxilar metálica; G3- Micro-ondas; G4- HH bi-maxilar micro ondas. Ciclo de polimerização para G1 e G2, água a 65ºC por 30 minutos, aquecimento interrompido por 30 minutos, reaquecimento a 65ºC por 30 minutos, seguido de água fervente por 1 hora. Para G3 e G4, micro ondas (20 minutos a 140 W e 5 minutos a 560 W). As medidas foram avaliadas com microscópio comparador linear. A distância final entre os dentes foi obtida subtraindo o valor da distância antes do processamento da prótese do valor da distância resultante do deslocamento dentário após o processamento. A diferença obtida entre essas distâncias foi submetida à ANOVA de 2 fatores, considerando como variáveis tipo de mufla e tipo de prótese. A prótese maxilar apresentou maior deslocamento dental quando comparada à mandibular. Os tipos de muflas e a interação com os tipos de próteses mostraram movimentos dentais similares antes e depois da polimerização. Em conclusão, o deslocamento dental promovido por diferentes tipos de frascos em próteses curadas por diferentes ciclos de polimerização promoveu efeito semelhante na alteração da distância entre os dentes. Maior valor para a mudança de distância entre os dentes ocorreu na prótese maxilar.

Strategies for potential toughening of acrylic denture bases polymerized with microwave energy

Abstract Thiourethane additives have been shown to improve properties in several dental polymer applications. The aim of this study was to verify the effect of the addition of thiourethane oligomers and acrylamide or isobornyl-based plasticizers on the physical properties of the denture base acrylic resin polymerized with microwaves. Thiourethane oligomer (TU) was synthetized and added to microwaved acrylic resin in proportions varying between 3 and 14 wt%. Separate experimental groups included the addition of dimethyl acrylamide (DMAM) and isobornyl methacrylate as plasticizers, at concentrations varying from 5 to 20 wt%. Samples were polymerized using microwave energy at 500 Watts for 3 min, deflasked at room temperature, stored in water at 37 °C for 24 h, and evaluated for: linear dimensional change, gloss, Knoop hardness, surface roughness, impact strength, yield strength, elastic modulus, toughness, yield strength, viscosity, glass transition temperature and network heterogeneity, and water sorption/solubility. Data were analyzed with ANOVA/Tukey's post-hoc test (a=5%). The addition of TU led to properties that were similar or worse than the materials to which it was not added, except for dimensional stability. The impact on properties was statistically significant for all materials above 20% addition of TU. The addition of DMAM at 5 wt% or isobornyl methacrylate at 10 wt% improved yield strength and modulus, but increased water sorption and solubility. Except for dimensional stability, the addition of thiourethane oligomers to acrylic denture base materials compromised most tested properties. The use of DMAM and isobornyl methacrylate improved properties for selected compositions.

Resumo Aditivos de tiouretano demonstraram melhorar propriedades de polímeros em diversas aplicações. O objetivo deste estudo foi verificar o efeito da adição de oligômeros de tiouretano, monômeros de acrilamida ou baseados em funcionalidade isobornil na propriedades físicas de bases de dentadura de acrílico polimerizadas em micro-ondas. O oligômero de tiouretano (TU) foi sintetizado e adicionado à resina acrílica em proporções variando de 3 a 14% em peso. Dimetil acrilamida (DMAM) e isobornil metacrilato (IBMA) foram adicionados em formulações separadas como plastificantes em concentrações variando de 5 a 20% em peso. As amostras foram polimerizadas usando energia de micro-ondas (500 Watts oor 3 min), desincluídas da mufla a temperature ambiente, armazenadas em água a 37°C por 24 h, e submetidas aos testes de: alteração dimensional linear, brilho, dureza Knoop, rugosidade superficial, resistência ao impacto, tensão normal de escoamento, módulo de elasticidade, tenacidade, viscosidade, temperatura de transição vítrea e heterogeneidade da rede polimérica, além de sorção de água e solubilidade. Os dados foram analisados com ANOVA e teste de Tukey (a=5%). A adição de TU não afetou ou diminuiu todas as propriedades, exceto pela estabilidade dimensional. O impacto nas propriedades foi estatisticamente significante para todos os materiais em concentrações acima de 20% de TU. Isso pode ser explicado por um encurtamento das cadeias e diminuição do empacotamento das cadeias lineares do PMMA. A adição de 5% de DMAM ou 10% de isobornil metacrilato melhoraram a tensão de escoamento e o módulo, mas aumentaram a sorção de água e solubilidade. Exceto pela estabilidade dimensional, a adição de oligômeros de tiouretano à bases de dentatura compostas por resina acrílica prejudicou todas a propriedades testadas. O uso de DMAM e isobornil metacrilato melhorou as propriedades para composições selecionadas.

Photoelastic and finite element stress analysis reliability for implant-supported system stress investigation

Aim: To compare the reliability between photoelastic and finite element (FE) analyses by evaluating the effect of different marginal misfit levels on the stresses generated on two different implant-supported systems using conventional and short implants. Methods: Two photoelastic models were obtained: model C with two conventional implants (4.1×11 mm); and model S with a conventional and a short implant (5×6 mm). Three-unit CoCr frameworks were fabricated simulating a superior first pre-molar (P) to first molar (M) fixed dental prosthesis. Different levels of misfit (µm) were selected based on the misfit average of 10 frameworks obtained by the single-screw test protocol: low (<20), medium (>20 and <40) and high (>40). Stress levels and distribution were measured by photoelastic analysis. A similar situation of the in vitro assay was designed and simulated by the in silico analysis. Maximum and minimum principal strain were recorded numerically and color-coded for the models. Von Mises Stress was obtained for the metallic components. Results: Photoelasticity and FE analyses showed similar tendency where the increase of misfit generates higher stress levels despite of the implant design. The short implant showed lower von Mises stress values; however, it presented stresses around its full length for the in vitro and in silico analysis. Also, model S showed higher µstrain values for all simulated misfit levels. The type of implant did not affect the stresses around pillar P. Conclusions: Photoelasticity and FEA are reliable methodologies presenting similarity for the investigation of the biomechanical behavior of implant-supported rehabilitations

Repair Strength in Simulated Restorations of Methacrylate- or Silorane-Based Composite Resins

Abstract The study verified the bond strength in simulated dental restorations of silorane- or methacrylate-based composites repaired with methacrylate-based composite. Methacrylate- (P60) or silorane-based (P90) composites were used associated with adhesive (Adper Single Bond 2). Twenty-four hemi-hourglass-shaped samples were repaired with each composite (n=12). Samples were divided according to groups: G1= P60 + Adper Single Bond 2+ P60; G2= P60 + Adper Single Bond 2 + P60 + thermocycling; G3= P90 + Adper Single Bond 2 + P60; and G4= P90 + Adper Single Bond 2 + P60 + thermocycling. G1 and G3 were submitted to tensile test 24 h after repair procedure, and G2 and G4 after submitted to 5,000 thermocycles at 5 and 55 ?#61616;C for 30 s in each bath. Tensile bond strength test was accomplished in an universal testing machine at crosshead speed of 0.5 mm/min. Data (MPa) were analyzed by two-way ANOVA and Tukey's test (5%). Sample failure pattern (adhesive, cohesive in resin or mixed) was evaluated by stereomicroscope at 30?#61655; and images were obtained in SEM. Bond strength values of methacrylate-based composite samples repaired with methacrylate-based composite (G1 and G2) were greater than for silorane-based samples (G3 and G4). Thermocycling decreased the bond strength values for both composites. All groups showed predominance of adhesive failures and no cohesive failure in composite resin was observed. In conclusion, higher bond strength values were observed in methacrylate-based resin samples and greater percentage of adhesive failures in silorane-based resin samples, both composites repaired with methacrylate-based resin.

Resumo O objetivo neste estudo foi verificar a resistência de união em restaurações simuladas de compósitos baseados em metacrilato ou silorano reparadas com compósito à base de metacrilato. Compósitos baseados em metacrilato (Filtek P60; 3M ESPE) ou silorano (Filtek P90; 3M ESPE) foram associados com adesivo (Adper Single Bond 2; 3M ESPE). Vinte e quatro amostras em forma de semi-ampulhetas foram reparadas com cada material (n=12), conforme os grupos experimentais: G1- P60 + Adper Single Bond 2 + P60; G2- P60 + Adper Single Bond 2 + P60 + termociclagem; G3- P90 + Adper Single Bond 2 + P60; e G4- P90 + Adper Single Bond 2 + P60 + termociclagem. Os grupos G1 e G3 foram submetidos ao ensaio de tração após 24 horas do procedimento de reparo e os grupos G2 e G4 depois de submetidos a 5.000 ciclos térmicos de 5 e 55 ?#61616;C por 30 s em cada banho. O teste de resistência à tração foi efetuado em máquina universal atuando numa velocidade de 0,5 mm/min. Os dados (MPa) foram submetidos a ANOVA a dois fatores e teste de Tukey (5%). O padrão de fratura das amostras (adesivo, coesivo em resina ou misto) foi avaliado em estereomicroscópio com aumento de 30x e imagens representativas foram obtidas em MEV. Os valores de resistência à tração das amostras feitas com compósito à base de metacrilato e reparadas com compósito à base de metacrilato (G1 e G2) foram maiores do que nas amostras feitas com compósito à base de silorano e reparadas nas mesmas condições (G3 e G4). A termociclagem diminuiu os valores de resistência à tração para ambos os compósitos. Todos os grupos mostraram predominância de fraturas adesivas e nenhuma falha coesiva foi observada em compósito. Em conclusão, valores maiores de resistência à tração foram observados em amostras de resina à base de metacrilato e maior porcentagem de fraturas adesivas nas amostras de resina à base de silorano, ambos os compósitos reparados com resina à base de metacrilato.

Effect of Polymerization Cycles on Gloss, Roughness, Hardness and Impact Strength of Acrylic Resins

Abstract The aim of this study was to evaluate the conventional and boiled polymerization cycles on gloss, roughness, hardness and impact strength of acrylic resins. Samples were made for each Classico and QC-20 materials (n=10) in dental stone molds obtained from rectangular metallic matrices embedded in metallic flasks. The powder-liquid ratio and manipulation of the acrylic resins' were accomplished according to manufacturers' instructions and the resins were conventionally packed in metallic flasks. After polymerization by (1) conventional: 74 °C for 9 h (Classico) and (2) boiled: 20 min (QC-20) cycles, the samples were deflasked after cooling at room temperature and conventionally finished and polished. The properties were evaluated after storage in water at 37 °C for 24 h. Gloss was verified with Multi Gloss 268 meter (Konica Minolta), surface roughness was measured with Surfcorder SE 1700 rugosimeter (Kosaka), Knoop hardness number was obtained with HMV-200 microdurometer, and impact strength was measured in an Otto Wolpert-Werke device by Charpy system (40 kpcm). Data were subjected to Student's t-test (at α=0.05). The results were: Gloss: 67.7 and 62.2 for Classico and QC-20 resins, respectively; Surface roughness: 0.874 and 1.469 Ra-µm for Classico and QC-20, respectively; Knoop hardness: 27.4 and 26.9 for Classico and QC-20, respectively; and Impact strength: 37.6 and 33.6 kgf/cm2 for Classico and QC-20, respectively. No statistically significant difference (p>0.05)were found between the resins for the evaluated properties. In conclusion, conventional and boiled polymerization cycles had similar effects on gloss, roughness, hardness and impact strength of both Classico and QC-20 resins.

Resumo O propósito neste estudo foi avaliar os ciclos de polimerização convencional e por fervura sobre o brilho, rugosidade, dureza e resistência ao impacto de resinas acrílicas. Amostras foram confeccionadas para cada resina Clássico ou QC-20 (n=20) em moldes de gesso obtidos de matrizes metálicas retangulares incluídas em muflas metálicas. A proporção monômero/polímero das resinas e manipulação foram de acordo com as recomendações dos fabricantes e a massa convencionalmente incluída em muflas metálicas. Após polimerização nos ciclos (1) convencional: 74 °C por 9 horas (Clássico) e (2) fervura: 20 min (QC-20), as amostras foram demufladas após esfriadas em temperatura ambiente e convencionalmente acabadas e polidas. As propriedades foram avaliadas após armazenagem das amostras em água a 37 °C por 24 h. O brilho foi verificado com medidor Multi Gloss 268 (Konica Minolta), a rugosidade avaliada com rugosímetro Surfcorder SE 1700 (Kosaka), a dureza Knoop foi obtida com microdurômetro HMV-200 (Shimadzu) e a resistência ao impacto determinada pelo sistema Charpy (Otto Wolpert Werke). Os dados submetidos ao teste t de Student (α=0.05) mostraram que Os resultados foram: brilho: 67,7 e 62,2 para Clássico e QC-20, respectivamente; rugosidade: 0,874 e 1,469 Ra-µm para Clássico e QC-20, respectivamente; dureza: 27,4 e 26,9 para Clássico e QC-20, respectivamente; e resistência ao impacto: 37,6 e 33,6 kgf/cm2 para Clássico e QC-20, respectivamente. Não houve diference estatisticamente significante entre as resinas para as propriedades avaliadas. Conclui-se que os ciclos de polimerização convencional e por fervura promoveram similares efeitos sobre o brilho, rugosidade, dureza e resistência ao impacto para ambas as resinas Clássico e QC-20.

Chemical analysis and Vickers hardness of orthodontic mini-implants

Orthodontic mini-implants are used in clinical practice to provide efficient and aesthetically-pleasing anchorage. AIM: To evaluate the hardness Vickers hardness and chemical composition of mini-implant titanium alloys from five commercial brands. METHODS: Thirty self-drilling mini-implants, six each from the following commercial brands, were used: Neodent NEO, Morelli MOR, Sin SIN, Conexão CON, and Rocky Mountain RMO. The hardness and chemical composition of the titanium alloys were performed by the Vickers hardness test and energy dispersive X-ray spectroscopy, respectively. RESULTS: Vickers hardness was significantly higher in SIN implants than in NEO, MOR, and CON implants. Similarly, VH was significantly higher in RMO implants than in MOR and NEO ones. In addition, VH was higher in CON implants than in NEO ones. There were no significant differences in the proportions of titanium and aluminum in the mini-implant alloy of the five commercial brands. Conversely, the proportion of vanadium differed significantly between CON and MOR/NEO implants. CONCLUSIONS: Mini-implants of different brands presented distinct properties of hardness and composition of the alloy...

Stress analysis of different configurations of 3 implants to support a fixed prosthesis in an edentulous jaw

This study's aims was to evaluate the stress distribution in a mandibular implant-supported prosthesis and peri-implant bone considering implant quantity, diameter and position using linear 3-D finite element analysis. Models of an anterior jaw comprised 4 groups according to implant quantity, diameter, and position: control group C, 5 regular implants; R, 3 regular implants; W, 3 wide implants; and DTR, 3 regular implants with the distal ones tilted 30º distally. The cantilever was loaded with an axial load of 50 N. Data was evaluated using von Mises stress on implants and maximum principal stress and microstrain on the bone. The W group showed the lowest value of maximum principal stress in peri-implant bone of the loaded side (4.64 MPa) when compared to C (5.27 MPa), DTR (5.94 MPa), and R (11.12 MPa). Lower stress values in the loaded implants were observed in the experimental groups when compared to the C group. However, the unloaded implants presented opposite results. All the screws of the W group presented lower stress values when compared to the C group. However, the R and DTR groups presented an increase in stress values with the exception of the loaded screw. A reduction in the number of implants associated with wider implants reduced the stress in the bone and prosthetic components.

Tratamento endodôntico na terceira idade / Endodontic treatment in elderly

A odontogeriatria é um ramo que cada vez mais vem tomando espaço na odontologia. Este segmento vem acompanhado de uma maior conscientização, tanto de profissionais quanto de pacientes, que passam a ter maiores preocupações com a saúde bucal, chegando à terceira idade com um maior número de dentes do que as gerações anteriores. Dessa forma, o cirurgião-dentista deve estar preparado para qualquer tipo de procedimento necessário para manter os seus pacientes com uma boa qualidade de saúde bucal. A endodontia, que em décadas passadas era muito pouco realizada em pacientes idosos, tem apresentado um crescente número de casos. Baseado nesse aumento de demanda, o presente trabalho realizou uma revisão da literatura quanto aos aspectos histológicos da polpa dental senil, do tratamento endodôntico propriamente dito e de aspectos sistêmicos que podem alterar o tratamento convencional, com o intuito de orientar o profissional que se dispõe a realizar estes procedimentos na prática diária.

Geriatric dentistry is in continuous diffusion in dentistry. It is followed by professionals conscious raising and by the patients preoccupations about oral health quality, keeping into their elderly which more teeth than the past generations. In this way the professional should be prepared to do any necessary procedure to patients keep their oral health quality. The endodontics, which few decades ago were rarely done in elderly is showing a considerable arouse in number of cases. Based on that increment on endodontics procedures the present paper reviewed the literature about the histological aspects of the elderly dental pulp, the endodontic procedure itself and some systemic aspects that may interfere anyhow in comparison with the conventional treatment, to guide the professional about these procedures in the daily practice.

Dimensional Accuracy of Stone Casts Made from Silicone-Based Impression Materials and Three Impression Techniques

The aim of this study was to measure and compare the dimensional accuracy of stone casts of a partially edentulous mandibular arch made by two condensation silicones, two addition silicones and three impression techniques (1-step putty/light-body, 2-step putty/light-body and monophase technique). A partially edentulous standard stainless steel mandibular arch cast was obtained with reference points on the permanent mandibular right and left canines, and permanent mandibular right and left second molars. The anteroposterior distances (between the mandibular left canine and second molar and between the mandibular right canine and second molar) and transverse distances (between the mandibular left and right canines and between the mandibular left and right second molars) of stainless steel cast were measured by a microscope at 30× magnification and 0.5 µm accuracy. All impressions were made with condensation or addition silicones. The 1- and 2-step putty/light-body impressions were accomplished with putty and light-body materials and the monophase impressions with light-body material only. After the impression procedures, accuracy of each material and technique was assessed measuring the stone casts poured (n=5) from the impressions, by the same microscope. The differences between the values of stone cast and stainless steel cast were calculated, presented as percentages and analyzed statistically by two-way ANOVA and the means compared by Tukey's test (α=0.05). All distances measured on stone casts showed altered dimensions with significantly negative linear changes (shrinkage) as compared to those of the stainless steel cast. The stone casts made from the addition silicones were dimensionally more accurate. No differences were found among the impression techniques.

O objetivo deste estudo foi mensurar e comparar a precisão dimensional de modelos de gesso de um arco mandibular parcialmente edêntulo feitos a partir de dois silicones por condensação, dois silicones por adição e três técnicas de moldagem (dupla mistura, reembasamento e moldeira individual). Um modelo metálico padrão de um arco mandibular parcialmente edêntulo foi obtido com pontos de referência nos caninos mandibulares permanentes esquerdo e direito, e segundo molares mandibulares permanentes esquerdo e direito. As distâncias anteroposteriores (entre o canino e segundo molar mandibulares esquerdos e entre o canino e segundo molar mandibulares direitos) e as distâncias transversais (entre os caninos mandibulares esquerdo e direito e entre os segundos molares mandibulares esquerdo e direito) do modelo metálico foram mensuradas através de um microscópio com 30x de aumento e 0,5 µm de precisão. Todas moldagens foram feitas com silicones por condensação e adição. As técnicas de dupla mistura e reembasamento foram realizadas com materiais nas viscosidades massa e leve e a técnica da moldeira individual somente com material leve. Após os procedimentos de moldagem, a precisão de cada material e técnica foi aferida medindo os modelos de gesso vazados (n=5) dos moldes, sob o mesmo microscópio. As diferenças entre os valores dos modelos de gesso e do modelo metálico foram calculadas, apresentadas como porcentagens e analisadas estatisticamente através da análise de variância e teste de Tukey (α=0,05). Todas as distâncias mensuradas nos modelos de gesso apresentaram dimensões alteradas com alterações lineares negativas (contração) significativas quando comparadas as medidas do modelo metálico. Os modelos de gesso feitos a partir de silicones por adição foram dimensionalmente mais precisos. Não foram encontradas diferenças entre as técnicas de moldagem.

Eficácia de diferentes solventes na dissolução de obturadores de canais radiculares / Efficacy of different solvents in dissolution of root canal sealers

O objetivo deste estudo foi avaliar a eficácia de solventes tradicionalmente utilizados (Hipoclorito de sódio – controle, Xilol e Eucaliptol) sobre obturadores de canais radiculares baseados em diferentes composições (óxido de zinco e eugenol, metacrilato (dois cimentos) e resina epóxica). Trinta amostras de cada material obturador foram divididas de maneira randomizada em três grupos (n=10), armazenadas por duas semanas em uma estufa para a secagem e imersas por 10 minutos em 1,0 ml de solvente. As amostras foram lavadas por 1 minuto em água corrente e novamente levadas à estufa por duas semanas. A perda da massa foi calculada com uma balança de precisão e os resultados submetidos à ANOVA dois fatores e ao teste Tukey com significância de 5%. Os resultados demonstraram que o tipo de material obturador não apresentou correlação à perda da massa (p> 0,05). Entretanto, o xilol teve um potencial de dissolução significante em relação aos solventes (p<0,05). Em relação aos materiais avaliados, pode-se concluir que os materiais obturadores não apresentam diferença no seu potencial de dissolução e que o xilol é o solvente mais eficaz

This study aimed to evaluate the efficacy of commonly utilised solvents (sodium hypochlorite - control, xylol and eucalyptol) on sealers based in different compositions (zincoxide-eugenol, methacrylate (two cements) and epoxy resin). Thirty samples of each cement were randomly divided in 3 groups (n=10), stored for 2 weeks in a chamber to set, immersed for 10 minutes in 1.0 mL of the solvent, washed for 1 minute in distilled water and stored in a new chamber for 2 weeks. The mass loss was calculated with a precision scale and the data subjected to 2-way ANOVA and Tukey’s test at 5% significance level. The results showed that the mass loss was not statistically significantly different among the sealers (p>0.05). However, the xylol potential was significantly higher among the solvents (p<0.05). Regarding the materials evaluated, it can be concluded that the sealers have no difference in their solving potential and xylol is the most effective solvent

Comparison of Silorane and Methacrylate-Based Composites on the Polymerization Heat Generated with Different Light-Curing Units and Dentin Thicknesses

This study evaluated the temperature variation in the pulp chamber during photoactivation of two restorative composite resins (Filtek P90 silorane-based composite and Heliomolar methacrylate-based composite) with either a quartz-tungsten-halogen (QTH) or light-emitting diodes (LED) light-curing unit (LCU) and using dentin thicknesses (0.5 and 1.0 mm). Standardized cavities (2x2x2 mm) were prepared in 80 bovine incisors, which were randomly assigned to 8 groups according to the photoactivation method and dentin thickness. Filtek P90 and Heliomolar (both in shade A3) were used with their respective adhesive systems (P90 self-etch primer / P90 adhesive bond and Excite adhesive). All experiments were carried out in a controlled environment (37°C). The temperature variations (°C) were recorded using a digital thermometer attached to a K-type thermocouple. The results were analyzed statistically by ANOVA and Tukey's test (α=0.05). For composite/dentin thickness interaction, temperature increase was significantly higher in 0.5 mm dentin thickness (40.07°C) compared with 1.0 mm dentin thickness (39.61°C) for Filtek P90. For composite/LCU interaction, the temperature increase was significantly higher for Filtek P90 (39.21°C - QTH and 40.47°C - LED) compared with Heliomolar (38.40°C - QTH and 39.30°C - LED). The silorane-based composite promoted higher temperature increase in the pulp chamber than the methacrylate-based composite.

Este estudo avaliou a variação de temperatura na câmara pulpar durante a fotoativação de duas resinas compostas (Filtek P90 – compósito à base de silorano e Heliomolar – compósito à base de metacrilato) com as unidades foto-ativadoras (UFs) luz de quartzo-tungstênio-halogênio (QTH) ou diodo emissor de luz (LED) e utilizando espessuras de dentina (0,5 e 1,0 mm). Cavidades padronizadas (2×2×2 mm) foram preparadas em 80 incisivos bovinos, as quais foram aleatoriamente divididas em 8 grupos de acordo com os métodos de fotoativação e espessura da dentina. Filtek P90 e Heliomolar (ambos na cor A3) foram utilizadas com seus respectivos sistemas adesivos (Primer P90 auto-condicionante / adesivo P90 e adesivo Excite). Todos os experimentos foram realizados em um ambiente controlado (37°C). As variações de temperatura (°C) foram mensuradas usando um termômetro digital conectado a um termopar tipo-K. Os resultados foram analisados estatisticamente por ANOVA e teste de Tukey (α=0,05). Para interação compósito/espessura de dentina, o aumento da temperatura foi estatisticamente superior para a espessura de dentina de 0,5 mm (40,07°C) quando comparado com a espessura de dentina de 1,0 mm (39,61°C) para a Filtek P90. Para a interação compósito/UFs, o aumento de temperatura foi estatisticamente superior para o Filtek P90 (39,21°C – QTH e 40,47°C – LED) quando comparado ao Heliomolar (38,40°C – QTH e 39,30°C – LED). Compósitos à base de silorano promovem maior aumento da temperatura na câmara pulpar em relação aos compósitos à base de metacrilato.

Stress Distribution in Co-Cr Implant Frameworks after Laser or TIG Welding

Lack of passivity has been associated with biomechanical problems in implant-supported prosthesis. The aim of this study was to evaluate the passivity of three techniques to fabricate an implant framework from a Co-Cr alloy by photoelasticity. The model was obtained from a steel die simulating an edentulous mandible with 4 external hexagon analog implants with a standard platform. On this model, five frameworks were fabricated for each group: a monoblock framework (control), laser and TIG welding frameworks. The photoelastic model was made from a flexible epoxy resin. On the photoelastic analysis, the frameworks were bolted onto the model for the verification of maximum shear stress at 34 selected points around the implants and 5 points in the middle of the model. The stresses were compared all over the photoelastic model, between the right, left, and center regions and between the cervical and apical regions. The values were subjected to two-way ANOVA, and Tukey's test (α=0.05). There was no significant difference among the groups and studied areas (p>0.05). It was concluded that the stresses generated around the implants were similar for all techniques.

Resumo A falta de passividade tem sido associada a problemas biomecânicos em próteses implantossuportadas. A proposta deste estudo foi avaliar, por meio da fotoelasticidade, a influência de três diferentes de fabricação de infraestrutura em liga de Co-Cr na passividade destas. O modelo foi obtido a partir de uma matriz de aço simulando uma mandíbula edêntula com 4 análogos de implantes de hexágono externo com plataforma padrão. Neste modelo, foram confeccionados cinco amostras para cada grupo: infraestruturas em monobloco, infraestruturas soldadas a laser e soldadas a TIG. O modelo fotoelástico foi feito com uma resina epóxi flexível (GIII, Polipox Industria e Comercio Ltda.). Na análise fotoelástica, as infraestruturas foram aparafusadas no modelo para a verificação da tensão de cisalhante máxima em 34 pontos selecionados ao redor dos implantes e 5 pontos na região média do modelo. Foram comparadas as tensões em todo o modelo fotoelástico, entre as regiões direita, esquerda e centro e também entre as regiões cervical e apical. Os valores foram submetidos à análise de variância a dois critérios, seguido pelo teste de Tukey (α=0,05). Os resultados não mostraram diferença significativa entre as tensões presentes nos grupos e nas áreas estudadas. Conclui-seque as tensões geradas ao redor dos implantes foram semelhantes entre as diferentes técnicas de confecção e entre todas as regiões analisadas. .

Linear dimensional change, compressive strength and detail reproduction in type IV dental stone dried at room temperature and in a microwave oven

The type IV dental stone is widely used for the fabrication of dyes and master casts for fixed and removable partial prostheses. It is typically normal to wait at least 24 hours for the casts to dry prior to beginning the laboratory procedures. The waiting time has been shown to be greatly reduced by using microwave drying. OBJECTIVE: This study evaluated the influence of drying techniques at room temperature and microwave oven on the linear dimensional change, compressive strength and detail reproduction in type IV dental stones. MATERIAL AND METHODS: Three type IV dental stone brands were selected; elite Rock, Shera Premium and Durone IV. Two different drying protocols were tested in 4 groups (n=10); G1 - room temperature (25±4ºC) dried for 2 hours; G2 - room temperature dried for 24 hours; G3 - room temperature dried for 7 days and G4 - microwave oven dried at 800 W for 5 minutes and after 2 hours at room temperature. After drying, the samples were assayed for dimensional charges. The sample surface was submitted to the ImageTool 3.0 software for compressive strength in a universal testing machine with a cell load of 50 KN at a crosshead speed of 0.5 mm/minutes and the detail reproduction was analyzed with a stereomicroscope at 25x magnification. The statistical analysis of the linear dimensional change and compressive strength data were conducted by the ANOVA test followed by the Tukey test (p<0.05). Detailed reproduction values were reported in percentages. RESULTS: For the compressive strength test, Elite Rock and Durone IV did not present significant differences between G2 and G4, while Shera Premium did not present differences between G3 and G4. The best reproduction levels were observed for G3. CONCLUSIONS: Dental stone microwave oven drying showed a linear dimensional change similar to after room temperature drying for 24 hours and 7 days. The compressive strength of the stone dried in the microwave oven was similar to those dried at room temperature for 24 hours, with the exception of Shera Premium, which had similar results for microwave and room temperature drying for 7 days. For the microwave drying method the detail reproduction levels for samples dried at room temperature for 24 hours and 7 days were similar, except for the Durone IV.

Análise das tensões ao redor de implantes após aparafusamento de infraestruturas soldadas a Laser e a Tig / Analysis of stresses around implants after screw infrastructure and Tig welded Laser

Objetivo: avaliar por meio da fotoelasticidade, as tensões geradas ao redor de implantes após o aparafusamento de estruturas confeccionadas por soldagem a Laser ou a TIG de barras cilíndricas de Cobalto-Cromo. Metodologia: foi realizado um estudo experimental a partir de um modelo de trabalho com dois implantes rosqueáveis. Nele foram realizadas a união dos UCLAs calcináveis à barra metálica, ambos de Cobalto-Cromo, por meio de soldagens à Laser(Grupo 1) e a TIG (Grupo 2), para confecção das amostras. Em seguida, sobre um modelo fotoelástico foram parafusadas as estruturas metálicas com torque manual de 20 Ncm, levadas ao polariscópio circular e submetidas a fotografias digitais padronizadas .Resultados: foi constatada a presença de tensões em ambos os grupos, contudo, a solda TIG exibiu maior número de franjas entre os implantes e nas cervicais distais. Conclusão: a estrutura confecciona por soldagem a Laser gerou menos tensões ao redor dos implantes que a confeccionada por soldagem a TIG para as infraestruturas de Co-Cr.

Aim: evaluate by using photoelasticity, the influence of laser welding or TIG welding of cylindrical rods of Cobalt-Chromium in the generation of tensions around implants. Methodology: using a working model with two screw implants, Cobalt-Chrome frameworks were made by laser welding method (Group 1) and TIG method(Group 2). Then, on a photoelastic model were bolted steel structures with manual torque of 20 Ncm, put to the circular polariscope and subjected to standardized digital photographs.Results: confirmed the presence of tensions in both groups, however, the TIG welding exhibited higher number of fringes between the implants and the distal neck. Conclusion: laser welding framework has generated less tension on the implants that the TIG welding for Cobalt-Chrome framework.

Efeitos da plataforma switching em reabilitações implantossuportadas - revisão de literatura / Effects of platform switching in implant-supported rehabilitations - a literature review

Objetivo: o objetivo deste estudo foi avaliar os efeitos do uso da plataforma switching em reabilitações implantossuportadas. Esse tipo de sistema consiste em utilizar um componente protético de menor diâmetro, conectado à plataforma de implante com maior diâmetro, portanto, não combinados como de maneira convencional. Revisão de literatura: foram selecionados 13 artigos publicados no período de 2006 a 2011 abrangendo as consequências do uso da plataforma switching em relação aos fatores biológicos e biomecânicos das reabilitações implantossuportadas. Considerações finais: ficaram claros os benefícios e a indicação do uso de tal sistema, destacando-se a redução na reabsorção inicial da crista óssea peri-implantar e manutenção desse nível ósseo ao longo dos anos, bem como a diminuição nas forças sobre o tecido ósseo adjacente à região cervical do implante. Sendo assim, mesmo na presença de possíveis inconvenientes causados por este sistema, como o aumento das tensões na região do parafuso e componente protético, o uso da plataforma switching torna-se um atrativo para as reabilitações protéticas implantossuportadas.

Solução protética para implantes mal posicionados: relato de caso clínico / Prosthetic solution for misplaced implants: a case report

Reabilitações protéticas sobre implantes ainda é um desafio para Odontologia. Existem situações em que os implantes são colocados em locais não compatíveis com o posicionamento dos dentes no arco, sendo necessário utilizar compensações protéticas capazes de corrigir essa dificuldade. Este trabalho tem como objetivo, relatar um caso clínico que apresenta uma opção protética para compensar o mau posicionamento dos implantes, pelo uso de uma mesoestrutura metálica. O paciente apresentava uma deformação óssea na região anterior de maxila onde foram instalados quatro implantes, posicionados de tal forma que os acessos aos parafusos protéticos ocorriam em áreas estética e biomecanicamente desfavoráveis. Portanto, foi planejado a confecção de uma mesoestrutura metálica, alterando a região de acesso aos parafusos protéticos, o que proporcionou ótimo resultado estético e satisfação do paciente.

Prosthetic rehabilitation on implants is still a challenge for Dentistry. There are situations where the implants are placed in locations that are not compatible with the positioning of the teeth in the arch, prosthetic compensation is necessary to be able to fix this problem. This study aims, report a clinical case that presents a prosthetic option to compensate the poor positioning of implants, by using a metallic mesostructure.The patient had a bone deformation in the anterior maxilla where four implants were installed, positioned so that access to prosthetic screws occurred in areas aesthetics and biomechanically unfavorable. So it was planned the construction of a metallic mesostructure, changing the area of access to prosthetic screws, which provided excellent aesthetic results and patient satisfaction.

Prótese destacável com sistema “Swivel Loc” – relato de caso clínico / Detachable prosthesis with Swivel Loc system – a clinical case report

A reabilitação total maxilar com próteses implantossuportadas representa em algumas situações clínicas dificuldades quanto a estética, fonética, suporte labial e higienização. As próteses destacáveis implantossuportadas são uma opção de tratamento frente a essa situação, onde o uso de encaixes permite a conexão entre uma prótese removível e uma infraestrutura metálica, sendo estéticos e funcionalmente eficientes. O objetivo deste trabalho foi de apresentar por meio de um caso clínico a confecção de uma protese destacável do sistema “Swivel Loc” como alternativa de aperfeiçoar a previsibilidade dessas reabilitações

The total rehabilitation of maxilla with supported implant prostheses represent in some clinical difficulties regarding aesthetics, phonetics, lip support and hygiene. The detachable implant supported dentures are a treatment option when faced with this situation, the use of attachments allows a connection between a removable prosthesis and a metallic infrastructure, being aesthetic and functionally efficient. The aim of this work was present through a clinical case the making of a detachable prosthesis with Swivel Loc system as an alternative to improve the predictability of these rehabilitations